irradiation defect meaning in English

辐照缺陷

The new vibrational infrared absorption band was assigned to local vibrational modes related to the complicated complex of irradiation defects that did not contain oxygen atoms
该峰只与辐照有关，对应复杂辐照缺陷， 400退火可以基本消除。
Irradiation defects decompounded and recombined with oxygen impurity and large quantity of nucleation centers were introduced in czsi bulk during annealing at 1100 . in nitrogen atmosphere , more defects were induced in fast neutron irradiated czsi than in argon atmosphere
不同气氛下快中子辐照直拉硅中缺陷形成的差异很大， 1100的高温退火中，与氩气氛相比，氮气氛退火样品中出现了更多缺陷。
Interact of fast - neutron irradiation defects and oxygen impurity in cz - silicon was investigated in this paper . the result suggested that oxygen precipitation formed at high temperature was promoted by fast - neutron irradiation obviously . compared with ntdczsi , fast neutron irradiation accelerated precipitation in czsi much more
本文对快中子辐照直拉硅中的缺陷和氧的相互作用进行了研究，快中子辐照促进了直拉硅中的氧沉淀，与以往ntdczsi研究结果相比，其促进作用更加明显。